In this work, the electrochromic and structural properties of NiO thin films prepared using optimized low value
electrodeposition parameters were studied. The optimized parameters were deposition current density, molar
concentration of nickel nitrate solution, and deposited charge density. The highest electrochromic characteristics
corresponded to deposition parameters of −0.05 mA/cm2 deposition current density, 0.02M of Ni(NO3)2.6H2O
solution, and charge density of 80 mC/cm2. For this optimized film, at 630 nm wavelength, the transmittance
modulation ΔT was 76%, the efficiency η was 19 cm2/C, the charge reversibility Qc/Qa was 97%, and a remarkable
contrast ratio CR of 5.9. In addition, a good cycling stability was confirmed up to 900 cycles.
Optimized NiO thin films were poorly crystallized exhibiting a nano-flake structure, high porosity, and homogeneity.

العنوان

Solid State Ionics

الناشر

Elsiever

بلد الناشر

هولندا

Indexing

Thomson Reuters

معامل التأثير

2,889

نوع المنشور

مطبوع فقط

المجلد

343

السنة

2019

الصفحات

1-10